| Product No. |
Product name |
Appearance |
Component |
Curing or drying time |
Viscosity
(25℃, Brookfield) |
Characteristics |
Applications |
| F-51 |
Leather impregnation |
Milky white viscous liquid |
Acrylic copolymer |
70~90℃ × 3~5mins |
<100cps No.1, 60rpm |
Resin saving. Good performance. Complete and quick coagulation on contacting with formic acid |
Leather impregnation |
| F-2200 |
Binder for leather finish |
70~90℃ × 3~5mins |
<200cps No.1, 30rpm |
Formaldehyde-free. Good adhesion. Bonding thermoplastic. Good handling. Give gloss & beauty to leather products |
For leather surface finish(Primer) |
| F-2202 |
Slightly transparent
liquid |
100~130â„ƒ× 5~7mins |
2000~4500cps
No.4,60rpm |
High gloss. Good leveling. Good platen release |
Shiny printing of leather |
| F-50 |
70~90℃ × 3~5mins |
<50cps
No.1,60rpm |
Small particle size. Good penetrability. |
Leather finish (bottom coat) |
| F-50-1 |
70~90℃ × 3~5mins |
<50cps
No.1,60rpm |
Small particle size. Good penetrability. Formaldehyde_free.APEO-free |
| F-57 |
120â„ƒ× 5mins |
<500cps
No.2,60rpm |
Anti- blocking. Embossing with clear patterns. Solvent resistance |
Decoration Of rubber surface |
| F-58 |
120â„ƒ× 5mins |
<100cps No.2, 60rpm |
Thermoplastic. Mid-hardness .Low blocking. Good platen release |
For Leather Finish (middle & top Coat) |
| F-52 |
Immersion resin |
70~90℃ × 3~5mins |
<50cps
No.2,60rpm |
Softness. Penetrability. Resistance of surface loosing. |
Resistance of leather surface to crack and loose |